data_ig_goosb_hta_0m 
 
_audit_creation_method            SHELXL-97 
_chemical_name_systematic 
; 
 ? 
; 
_chemical_name_common             ? 
_chemical_melting_point           ? 
_chemical_formula_moiety          ? 
_chemical_formula_sum 
 'H10 Al2 Ca O21 Si6' 
_chemical_formula_weight          608.66 
 
loop_ 
 _atom_type_symbol 
 _atom_type_description 
 _atom_type_scat_dispersion_real 
 _atom_type_scat_dispersion_imag 
 _atom_type_scat_source 
 'O'  'O'   0.0106   0.0060 
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 
 'H'  'H'   0.0000   0.0000 
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 
 'Al'  'Al'   0.0645   0.0514 
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 
 'Si'  'Si'   0.0817   0.0704 
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 
 'Ca'  'Ca'   0.2262   0.3064 
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 
 
_symmetry_cell_setting            ? 
_symmetry_space_group_name_H-M    ? 
 
loop_ 
 _symmetry_equiv_pos_as_xyz 
 'x, y, z' 
 '-x, y+1/2, -z' 
 
_cell_length_a                    7.2226(2) 
_cell_length_b                    16.3708(5) 
_cell_length_c                    14.2624(4) 
_cell_angle_alpha                 90.00 
_cell_angle_beta                  101.630(2) 
_cell_angle_gamma                 90.00 
_cell_volume                      1651.76(8) 
_cell_formula_units_Z             4 
_cell_measurement_temperature     172(2) 
_cell_measurement_reflns_used     ? 
_cell_measurement_theta_min       ? 
_cell_measurement_theta_max       ? 
 
_exptl_crystal_description        ? 
_exptl_crystal_colour             ? 
_exptl_crystal_size_max           ? 
_exptl_crystal_size_mid           ? 
_exptl_crystal_size_min           ? 
_exptl_crystal_density_meas       ? 
_exptl_crystal_density_diffrn     2.448 
_exptl_crystal_density_method     'not measured' 
_exptl_crystal_F_000              1232 
_exptl_absorpt_coefficient_mu     1.041 
_exptl_absorpt_correction_type    ? 
_exptl_absorpt_correction_T_min   ? 
_exptl_absorpt_correction_T_max   ? 
_exptl_absorpt_process_details    ? 
 
_exptl_special_details 
; 
 ? 
; 
 
_diffrn_ambient_temperature       172(2) 
_diffrn_radiation_wavelength      0.71073 
_diffrn_radiation_type            MoK\a 
_diffrn_radiation_source          'fine-focus sealed tube' 
_diffrn_radiation_monochromator   graphite 
_diffrn_measurement_device_type   ? 
_diffrn_measurement_method        ? 
_diffrn_detector_area_resol_mean  ? 
_diffrn_reflns_number             14054 
_diffrn_reflns_av_R_equivalents   0.0573 
_diffrn_reflns_av_sigmaI/netI     0.0640 
_diffrn_reflns_limit_h_min        -8 
_diffrn_reflns_limit_h_max        8 
_diffrn_reflns_limit_k_min        -18 
_diffrn_reflns_limit_k_max        18 
_diffrn_reflns_limit_l_min        -15 
_diffrn_reflns_limit_l_max        15 
_diffrn_reflns_theta_min          1.92 
_diffrn_reflns_theta_max          23.45 
_reflns_number_total              4819 
_reflns_number_gt                 4634 
_reflns_threshold_expression      >2sigma(I) 
 
_computing_data_collection        ? 
_computing_cell_refinement        ? 
_computing_data_reduction         ? 
_computing_structure_solution     'SHELXS-97 (Sheldrick, 2008)' 
_computing_structure_refinement   'SHELXL-97 (Sheldrick, 2008)' 
_computing_molecular_graphics     ? 
_computing_publication_material   ? 
 
_refine_special_details 
; 
 Refinement of F^2^ against ALL reflections.  The weighted R-factor wR and 
 goodness of fit S are based on F^2^, conventional R-factors R are based 
 on F, with F set to zero for negative F^2^. The threshold expression of 
 F^2^ > 2sigma(F^2^) is used only for calculating R-factors(gt) etc. and is 
 not relevant to the choice of reflections for refinement.  R-factors based 
 on F^2^ are statistically about twice as large as those based on F, and R- 
 factors based on ALL data will be even larger. 
; 
 
_refine_ls_structure_factor_coef  Fsqd  
_refine_ls_matrix_type            full 
_refine_ls_weighting_scheme       calc  
_refine_ls_weighting_details 
 'calc w=1/[\s^2^(Fo^2^)+(0.0475P)^2^+34.4526P] where P=(Fo^2^+2Fc^2^)/3' 
_atom_sites_solution_primary      direct 
_atom_sites_solution_secondary    difmap 
_atom_sites_solution_hydrogens    geom 
_refine_ls_hydrogen_treatment     mixed 
_refine_ls_extinction_method      none 
_refine_ls_extinction_coef        ? 
_refine_ls_abs_structure_details 
 'Flack H D (1983), Acta Cryst. A39, 876-881' 
_refine_ls_abs_structure_Flack    0.21(18) 
_refine_ls_number_reflns          4819 
_refine_ls_number_parameters      483 
_refine_ls_number_restraints      1 
_refine_ls_R_factor_all           0.0926 
_refine_ls_R_factor_gt            0.0902 
_refine_ls_wR_factor_ref          0.2208 
_refine_ls_wR_factor_gt           0.2192 
_refine_ls_goodness_of_fit_ref    1.207 
_refine_ls_restrained_S_all       1.207 
_refine_ls_shift/su_max           0.005 
_refine_ls_shift/su_mean          0.000 
 
loop_ 
 _atom_site_label 
 _atom_site_type_symbol 
 _atom_site_fract_x 
 _atom_site_fract_y 
 _atom_site_fract_z 
 _atom_site_U_iso_or_equiv 
 _atom_site_adp_type 
 _atom_site_occupancy 
 _atom_site_symmetry_multiplicity 
 _atom_site_calc_flag 
 _atom_site_refinement_flags 
 _atom_site_disorder_assembly 
 _atom_site_disorder_group 
Ca1 Ca 1.1889(6) 0.5900(2) 0.2424(3) 0.0336(16) Uani 0.838(15) 1 d P . . 
Ca2 Ca 1.5264(8) 0.1236(3) 0.2803(3) 0.053(2) Uani 0.809(17) 1 d P . . 
Si1 Si 1.3497(5) 0.3338(3) -0.0418(3) 0.0211(9) Uani 1 1 d . . . 
Si2 Si 1.2409(6) 0.6502(2) -0.0755(3) 0.0228(10) Uani 1 1 d . . . 
Si3 Si 0.9869(6) 0.5267(2) -0.0087(3) 0.0194(9) Uani 1 1 d . . . 
Si4 Si 1.5194(6) 0.2387(3) 0.6858(3) 0.0244(10) Uani 1 1 d . . . 
Si5 Si 1.4390(6) 0.4307(3) 0.3495(3) 0.0224(10) Uani 1 1 d . . . 
Si6 Si 1.3200(5) 0.7608(3) 0.1081(3) 0.0211(9) Uani 1 1 d . . . 
Al1 Al 0.6743(6) 0.6611(3) -0.0574(4) 0.0241(11) Uani 1 1 d . . . 
Al2 Al 1.2372(6) 0.4177(3) 0.1333(3) 0.0221(10) Uani 1 1 d . . . 
Si1B Si 1.8002(14) 0.3483(7) 0.4458(8) 0.034(2) Uani 0.50 1 d P . . 
Si1F Si 1.7550(13) 0.3164(6) 0.3766(7) 0.026(2) Uani 0.50 1 d P . . 
Si2B Si 1.8155(6) 0.6692(2) 0.4448(3) 0.0213(9) Uani 1 1 d . . . 
Si3B Si 1.5459(6) 0.5481(3) 0.5116(3) 0.0234(10) Uani 1 1 d . . . 
Si4B Si 1.0972(7) 0.2430(3) 0.1917(3) 0.0307(11) Uani 1 1 d . . . 
Si5B Si 1.0342(6) 0.8837(3) 0.1466(3) 0.0222(9) Uani 1 1 d . . . 
Si6B Si 1.1636(6) 0.2944(3) 0.3916(3) 0.0215(9) Uani 1 1 d . . . 
Al1B Al 1.2577(6) 0.6842(3) 0.4749(3) 0.0254(11) Uani 1 1 d . . . 
Al2B Al 1.7162(13) 0.4080(6) 0.6463(7) 0.020(2) Uani 0.50 1 d P . . 
Al2F Al 1.6413(15) 0.4242(6) 0.6896(8) 0.026(2) Uani 0.50 1 d P . . 
O1 O 1.3003(15) 0.2410(6) -0.0238(8) 0.027(2) Uani 1 1 d . . . 
O2 O 1.4382(13) 0.6357(6) -0.1092(8) 0.022(2) Uani 1 1 d . . . 
O3 O 0.8071(17) 0.5843(8) -0.0019(9) 0.040(3) Uani 1 1 d . . . 
O4 O 0.7438(16) 0.6844(8) -0.1618(9) 0.037(3) Uani 1 1 d . . . 
O5 O 0.8091(15) 0.8708(6) 0.1286(8) 0.026(2) Uani 1 1 d . . . 
O6 O 1.3699(15) 0.3901(7) 0.0506(7) 0.026(2) Uani 1 1 d . . . 
O7 O 1.4496(14) 0.8320(6) 0.0798(8) 0.023(2) Uani 1 1 d . . . 
O8 O 1.1267(14) 0.5657(6) -0.0708(8) 0.025(2) Uani 1 1 d . . . 
O9 O 1.1142(19) 0.7106(8) -0.1520(10) 0.048(3) Uiso 1 1 d . . . 
O10 O 1.2739(16) 0.6920(9) 0.0276(8) 0.046(4) Uani 1 1 d . . . 
O11 O 1.0811(15) 0.9406(7) 0.0599(8) 0.030(3) Uani 1 1 d . . . 
O12 O 1.1006(16) 0.5066(7) 0.0972(7) 0.031(3) Uani 1 1 d . . . 
O13 O 1.1161(17) 0.3326(8) 0.1596(7) 0.035(3) Uani 1 1 d . . . 
O14 O 1.4130(16) 0.7099(7) 0.2031(8) 0.029(3) Uani 1 1 d . . . 
O15 O 1.3519(16) 0.4595(7) 0.2416(8) 0.035(3) Uani 1 1 d . . . 
O16 O 1.3296(17) 0.3516(8) 0.3792(9) 0.045(4) Uani 1 1 d . . . 
O1B O 1.739(2) 0.2670(11) 0.4567(16) 0.099(8) Uani 1 1 d . . . 
O2B O 1.0242(15) 0.6498(7) 0.4365(8) 0.032(3) Uani 1 1 d . . . 
O3B O 1.4161(17) 0.6150(7) 0.5492(8) 0.033(3) Uani 1 1 d . . . 
O4B O 1.3437(15) 0.6865(7) 0.3705(8) 0.029(3) Uani 1 1 d . . . 
O5B O 1.6568(16) 0.4029(7) 0.3585(8) 0.032(3) Uani 1 1 d . . . 
O6B O 1.803(4) 0.376(2) 0.548(2) 0.069(13) Uiso 0.55(5) 1 d P . . 
O7B O 1.978(3) 0.3456(11) 0.3871(13) 0.080(5) Uiso 1 1 d . . . 
O8B O 1.7279(15) 0.5878(7) 0.4812(7) 0.029(3) Uani 1 1 d . . . 
O9B O 1.6928(15) 0.7027(7) 0.3414(7) 0.027(3) Uani 1 1 d . . . 
O10B O 1.7824(18) 0.7417(8) 0.5136(9) 0.045(3) Uani 1 1 d . . . 
O11B O 1.4135(17) 0.5067(8) 0.4193(9) 0.042(3) Uani 1 1 d . . . 
O12B O 1.613(2) 0.4890(10) 0.5994(14) 0.082(7) Uani 1 1 d . . . 
O13B O 1.5291(15) 0.3351(8) 0.6729(7) 0.033(3) Uani 1 1 d . . . 
O14B O 1.143(2) 0.2284(10) 0.3093(12) 0.070(5) Uiso 1 1 d . . . 
O15B O 1.1227(15) 0.9172(7) 0.2528(9) 0.037(3) Uani 1 1 d . . . 
O16B O 1.1272(16) 0.7963(7) 0.1272(8) 0.030(3) Uani 1 1 d . . . 
OA2F O 1.513(4) 0.4946(16) 0.7551(18) 0.042(10) Uiso 0.51(5) 1 d P . . 
OS1F O 1.674(3) 0.2496(15) 0.2979(16) 0.022(9) Uiso 0.43(4) 1 d P . . 
W1 O 0.908(2) 0.6607(10) 0.1988(12) 0.063(7) Uiso 0.94(5) 1 d P . . 
W2 O 1.883(5) 0.084(2) 0.308(2) 0.064(15) Uiso 0.44(5) 1 d P . . 
W4 O 0.978(4) 0.5102(18) 0.307(2) 0.083(12) Uiso 0.66(5) 1 d P . . 
W5 O 1.344(6) 0.493(2) 0.752(3) 0.062(16) Uiso 0.42(5) 1 d P . . 
 
loop_ 
 _atom_site_aniso_label 
 _atom_site_aniso_U_11 
 _atom_site_aniso_U_22 
 _atom_site_aniso_U_33 
 _atom_site_aniso_U_23 
 _atom_site_aniso_U_13 
 _atom_site_aniso_U_12 
Ca1 0.045(3) 0.011(2) 0.042(3) -0.0170(18) 0.005(2) 0.0008(17) 
Ca2 0.079(4) 0.059(4) 0.017(3) 0.010(2) 0.004(2) 0.032(3) 
Si1 0.013(2) 0.022(2) 0.029(2) 0.0005(19) 0.0059(17) -0.0050(17) 
Si2 0.023(2) 0.012(2) 0.034(2) 0.0084(18) 0.0091(19) 0.0043(17) 
Si3 0.022(2) 0.011(2) 0.025(2) 0.0071(17) 0.0042(17) 0.0034(17) 
Si4 0.026(2) 0.020(2) 0.027(2) -0.0074(19) 0.0067(19) -0.0027(19) 
Si5 0.022(2) 0.026(2) 0.019(2) 0.0021(18) 0.0044(17) -0.0031(18) 
Si6 0.013(2) 0.029(3) 0.020(2) 0.0020(18) 0.0010(16) 0.0040(17) 
Al1 0.012(2) 0.019(2) 0.040(3) -0.005(2) 0.003(2) 0.0063(19) 
Al2 0.024(2) 0.023(2) 0.019(2) 0.0016(19) 0.0020(19) 0.006(2) 
Si1B 0.029(5) 0.040(6) 0.036(6) 0.024(5) 0.014(4) 0.004(4) 
Si1F 0.027(5) 0.026(5) 0.029(5) 0.000(4) 0.016(4) -0.005(4) 
Si2B 0.018(2) 0.013(2) 0.030(2) 0.0017(18) -0.0013(17) 0.0041(17) 
Si3B 0.015(2) 0.023(2) 0.030(2) 0.0066(19) -0.0018(18) 0.0046(18) 
Si4B 0.034(3) 0.038(3) 0.025(2) -0.012(2) 0.018(2) -0.017(2) 
Si5B 0.017(2) 0.024(2) 0.025(2) 0.0015(18) 0.0028(18) 0.0005(18) 
Si6B 0.014(2) 0.021(2) 0.028(2) 0.0015(18) 0.0009(17) -0.0023(17) 
Al1B 0.024(3) 0.024(3) 0.032(3) -0.005(2) 0.013(2) -0.001(2) 
Al2B 0.009(5) 0.026(6) 0.027(5) 0.004(4) 0.010(4) 0.008(4) 
Al2F 0.020(5) 0.029(6) 0.023(6) 0.006(5) -0.013(5) -0.001(5) 
O1 0.031(6) 0.019(6) 0.034(6) 0.003(5) 0.009(5) 0.002(5) 
O2 0.013(5) 0.019(5) 0.040(6) -0.013(5) 0.019(5) -0.002(4) 
O3 0.042(7) 0.033(7) 0.042(7) -0.014(6) 0.005(6) 0.017(6) 
O4 0.031(6) 0.039(7) 0.050(8) -0.012(6) 0.030(6) 0.008(5) 
O5 0.026(6) 0.016(6) 0.036(6) -0.003(5) 0.005(5) 0.001(5) 
O6 0.030(6) 0.034(6) 0.014(5) 0.010(5) 0.005(4) 0.001(5) 
O7 0.020(5) 0.011(5) 0.042(6) -0.005(5) 0.015(5) -0.011(4) 
O8 0.017(5) 0.016(6) 0.043(7) -0.007(5) 0.005(5) -0.007(4) 
O10 0.032(7) 0.074(10) 0.036(7) -0.023(7) 0.013(6) -0.032(7) 
O11 0.026(6) 0.030(6) 0.040(7) 0.005(5) 0.021(5) -0.003(5) 
O12 0.031(6) 0.049(8) 0.012(5) 0.002(5) 0.003(5) -0.010(6) 
O13 0.050(7) 0.040(7) 0.013(5) 0.007(5) 0.005(5) -0.015(6) 
O14 0.041(7) 0.022(6) 0.028(6) 0.001(5) 0.013(5) 0.014(5) 
O15 0.038(7) 0.031(7) 0.029(6) 0.002(5) -0.009(5) 0.007(5) 
O16 0.030(7) 0.055(9) 0.048(8) 0.037(7) 0.003(6) -0.002(6) 
O1B 0.037(8) 0.095(14) 0.18(2) 0.109(14) 0.047(10) 0.013(9) 
O2B 0.025(6) 0.040(7) 0.028(6) 0.010(5) 0.002(5) 0.009(5) 
O3B 0.040(7) 0.025(6) 0.038(7) -0.004(5) 0.018(6) 0.005(5) 
O4B 0.036(6) 0.019(6) 0.030(6) 0.008(5) 0.004(5) -0.004(5) 
O5B 0.034(6) 0.033(7) 0.031(6) 0.011(5) 0.014(5) 0.013(5) 
O8B 0.022(6) 0.039(7) 0.029(6) 0.009(5) 0.009(5) 0.011(5) 
O9B 0.034(6) 0.026(6) 0.018(5) 0.007(5) -0.006(5) 0.005(5) 
O10B 0.039(7) 0.049(8) 0.037(7) -0.013(6) -0.013(5) 0.010(6) 
O11B 0.030(7) 0.046(8) 0.052(8) -0.004(6) 0.013(6) 0.017(6) 
O12B 0.037(8) 0.070(11) 0.130(16) 0.085(11) -0.005(9) -0.014(7) 
O13B 0.025(6) 0.045(7) 0.024(6) 0.009(5) -0.006(5) -0.004(5) 
O15B 0.028(6) 0.027(6) 0.056(8) -0.012(6) 0.006(6) -0.002(5) 
O16B 0.034(6) 0.023(6) 0.033(6) 0.013(5) 0.005(5) -0.004(5) 
 
_geom_special_details 
; 
 All esds (except the esd in the dihedral angle between two l.s. planes) 
 are estimated using the full covariance matrix.  The cell esds are taken 
 into account individually in the estimation of esds in distances, angles 
 and torsion angles; correlations between esds in cell parameters are only 
 used when they are defined by crystal symmetry.  An approximate (isotropic) 
 treatment of cell esds is used for estimating esds involving l.s. planes. 
; 
 
loop_ 
 _geom_bond_atom_site_label_1 
 _geom_bond_atom_site_label_2 
 _geom_bond_distance 
 _geom_bond_site_symmetry_2 
 _geom_bond_publ_flag 
Ca1 W1 2.312(17) . ? 
Ca1 W4 2.34(3) . ? 
Ca1 O15 2.440(12) . ? 
Ca1 O12 2.454(12) . ? 
Ca1 O4B 2.502(12) . ? 
Ca1 O14 2.675(12) . ? 
Ca1 O11B 3.034(14) . ? 
Ca1 Si4 3.248(6) 2_856 ? 
Ca1 Al2 3.273(6) . ? 
Ca1 Si5 3.359(6) . ? 
Ca1 Al1B 3.600(6) . ? 
Ca1 Si6 3.621(6) . ? 
Ca2 OA2F 2.18(3) 2_846 ? 
Ca2 OS1F 2.31(2) . ? 
Ca2 O3B 2.388(12) 2_846 ? 
Ca2 W5 2.41(4) 2_846 ? 
Ca2 O2 2.511(11) 2_845 ? 
Ca2 O4 2.514(13) 2_745 ? 
Ca2 W2 2.61(4) . ? 
Ca2 O12B 3.08(2) 2_846 ? 
Ca2 Al1 3.274(6) 2_745 ? 
Ca2 Si3B 3.353(7) 2_846 ? 
Ca2 Al2F 3.539(13) 2_846 ? 
Ca2 Al1B 3.662(7) 2_846 ? 
Si1 O6 1.590(11) . ? 
Si1 O1 1.593(11) . ? 
Si1 O5 1.626(11) 2_745 ? 
Si1 O7 1.647(10) 2_845 ? 
Si2 O10 1.595(12) . ? 
Si2 O2 1.611(9) . ? 
Si2 O9 1.614(14) . ? 
Si2 O8 1.619(10) . ? 
Si3 O12 1.601(11) . ? 
Si3 O8 1.603(11) . ? 
Si3 O11 1.618(12) 2_745 ? 
Si3 O3 1.624(12) . ? 
Si4 O13B 1.591(13) . ? 
Si4 O9B 1.615(12) 2_846 ? 
Si4 O14 1.630(12) 2_846 ? 
Si4 O4B 1.634(11) 2_846 ? 
Si4 Ca1 3.248(6) 2_846 ? 
Si5 O15 1.611(12) . ? 
Si5 O16 1.617(12) . ? 
Si5 O5B 1.618(12) . ? 
Si5 O11B 1.626(13) . ? 
Si6 O16B 1.583(12) . ? 
Si6 O10 1.594(13) . ? 
Si6 O7 1.598(10) . ? 
Si6 O14 1.617(11) . ? 
Al1 O3 1.680(13) . ? 
Al1 O4 1.708(12) . ? 
Al1 O1 1.733(11) 2_755 ? 
Al1 O2 1.766(10) 1_455 ? 
Al1 Ca2 3.274(6) 2_755 ? 
Al2 O6 1.723(11) . ? 
Al2 O13 1.725(12) . ? 
Al2 O15 1.739(12) . ? 
Al2 O12 1.776(13) . ? 
Si1B Si1F 1.106(14) . ? 
Si1B O1B 1.42(2) . ? 
Si1B O6B 1.52(3) . ? 
Si1B O7B 1.67(2) . ? 
Si1B O5B 1.704(14) . ? 
Si1F O1B 1.424(17) . ? 
Si1F O5B 1.581(14) . ? 
Si1F OS1F 1.59(3) . ? 
Si1F O7B 1.66(2) . ? 
Si2B O2B 1.568(12) 1_655 ? 
Si2B O10B 1.588(13) . ? 
Si2B O8B 1.605(12) . ? 
Si2B O9B 1.654(10) . ? 
Si3B O12B 1.579(14) . ? 
Si3B O3B 1.602(12) . ? 
Si3B O8B 1.602(12) . ? 
Si3B O11B 1.613(14) . ? 
Si3B Ca2 3.353(7) 2_856 ? 
Si4B O13 1.551(12) . ? 
Si4B O9 1.608(14) 2_745 ? 
Si4B O4 1.618(13) 2_745 ? 
Si4B O14B 1.661(17) . ? 
Si5B O5 1.608(11) . ? 
Si5B O15B 1.616(13) . ? 
Si5B O16B 1.628(12) . ? 
Si5B O11 1.637(11) . ? 
Si6B O16 1.560(13) . ? 
Si6B O7B 1.572(19) 1_455 ? 
Si6B O14B 1.580(17) . ? 
Si6B O10B 1.585(12) 2_846 ? 
Al1B O1B 1.667(14) 2_856 ? 
Al1B O4B 1.726(11) . ? 
Al1B O2B 1.757(12) . ? 
Al1B O3B 1.796(13) . ? 
Al1B Ca2 3.662(7) 2_856 ? 
Al2B Al2F 0.937(12) . ? 
Al2B O12B 1.600(17) . ? 
Al2B O15B 1.664(15) 2_846 ? 
Al2B O6B 1.73(3) . ? 
Al2B O13B 1.898(15) . ? 
Al2F O12B 1.649(16) . ? 
Al2F O13B 1.662(15) . ? 
Al2F O15B 1.740(14) 2_846 ? 
Al2F OA2F 1.85(3) . ? 
Al2F Ca2 3.539(13) 2_856 ? 
O1 Al1 1.733(11) 2_745 ? 
O2 Al1 1.766(10) 1_655 ? 
O2 Ca2 2.511(11) 2_855 ? 
O4 Si4B 1.618(13) 2_755 ? 
O4 Ca2 2.514(13) 2_755 ? 
O5 Si1 1.626(11) 2_755 ? 
O7 Si1 1.647(10) 2_855 ? 
O9 Si4B 1.608(14) 2_755 ? 
O11 Si3 1.618(12) 2_755 ? 
O14 Si4 1.630(12) 2_856 ? 
O1B Al1B 1.667(14) 2_846 ? 
O2B Si2B 1.568(11) 1_455 ? 
O3B Ca2 2.389(12) 2_856 ? 
O4B Si4 1.634(11) 2_856 ? 
O7B Si6B 1.572(19) 1_655 ? 
O9B Si4 1.615(12) 2_856 ? 
O10B Si6B 1.585(12) 2_856 ? 
O12B Ca2 3.08(2) 2_856 ? 
O15B Al2B 1.664(15) 2_856 ? 
O15B Al2F 1.740(14) 2_856 ? 
OA2F W5 1.21(4) . ? 
OA2F Ca2 2.18(3) 2_856 ? 
W5 Ca2 2.41(4) 2_856 ? 
 
loop_ 
 _geom_angle_atom_site_label_1 
 _geom_angle_atom_site_label_2 
 _geom_angle_atom_site_label_3 
 _geom_angle 
 _geom_angle_site_symmetry_1 
 _geom_angle_site_symmetry_3 
 _geom_angle_publ_flag 
W1 Ca1 W4 77.2(9) . . ? 
W1 Ca1 O15 146.7(5) . . ? 
W4 Ca1 O15 82.4(8) . . ? 
W1 Ca1 O12 89.2(5) . . ? 
W4 Ca1 O12 86.8(8) . . ? 
O15 Ca1 O12 63.5(4) . . ? 
W1 Ca1 O4B 96.9(5) . . ? 
W4 Ca1 O4B 107.1(8) . . ? 
O15 Ca1 O4B 114.3(4) . . ? 
O12 Ca1 O4B 165.7(4) . . ? 
W1 Ca1 O14 96.5(5) . . ? 
W4 Ca1 O14 164.6(8) . . ? 
O15 Ca1 O14 109.2(4) . . ? 
O12 Ca1 O14 107.3(4) . . ? 
O4B Ca1 O14 59.3(3) . . ? 
W1 Ca1 O11B 137.9(5) . . ? 
W4 Ca1 O11B 72.6(8) . . ? 
O15 Ca1 O11B 55.4(4) . . ? 
O12 Ca1 O11B 117.1(4) . . ? 
O4B Ca1 O11B 65.9(4) . . ? 
O14 Ca1 O11B 105.0(4) . . ? 
W1 Ca1 Si4 100.9(4) . 2_856 ? 
W4 Ca1 Si4 136.7(7) . 2_856 ? 
O15 Ca1 Si4 112.0(3) . 2_856 ? 
O12 Ca1 Si4 136.4(3) . 2_856 ? 
O4B Ca1 Si4 29.6(3) . 2_856 ? 
O14 Ca1 Si4 30.0(2) . 2_856 ? 
O11B Ca1 Si4 82.6(3) . 2_856 ? 
W1 Ca1 Al2 118.4(4) . . ? 
W4 Ca1 Al2 81.2(7) . . ? 
O15 Ca1 Al2 31.3(3) . . ? 
O12 Ca1 Al2 32.3(3) . . ? 
O4B Ca1 Al2 144.7(3) . . ? 
O14 Ca1 Al2 114.0(3) . . ? 
O11B Ca1 Al2 85.3(3) . . ? 
Si4 Ca1 Al2 132.17(18) 2_856 . ? 
W1 Ca1 Si5 150.9(5) . . ? 
W4 Ca1 Si5 73.8(7) . . ? 
O15 Ca1 Si5 26.7(3) . . ? 
O12 Ca1 Si5 88.7(3) . . ? 
O4B Ca1 Si5 92.2(3) . . ? 
O14 Ca1 Si5 111.9(3) . . ? 
O11B Ca1 Si5 28.9(2) . . ? 
Si4 Ca1 Si5 100.56(16) 2_856 . ? 
Al2 Ca1 Si5 56.51(12) . . ? 
W1 Ca1 Al1B 89.1(4) . . ? 
W4 Ca1 Al1B 81.6(7) . . ? 
O15 Ca1 Al1B 113.7(3) . . ? 
O12 Ca1 Al1B 168.4(3) . . ? 
O4B Ca1 Al1B 25.6(3) . . ? 
O14 Ca1 Al1B 84.3(3) . . ? 
O11B Ca1 Al1B 58.4(3) . . ? 
Si4 Ca1 Al1B 55.09(12) 2_856 . ? 
Al2 Ca1 Al1B 143.02(18) . . ? 
Si5 Ca1 Al1B 87.25(15) . . ? 
W1 Ca1 Si6 77.3(4) . . ? 
W4 Ca1 Si6 154.5(7) . . ? 
O15 Ca1 Si6 119.7(3) . . ? 
O12 Ca1 Si6 91.9(3) . . ? 
O4B Ca1 Si6 76.9(3) . . ? 
O14 Ca1 Si6 24.3(2) . . ? 
O11B Ca1 Si6 129.3(3) . . ? 
Si4 Ca1 Si6 50.65(11) 2_856 . ? 
Al2 Ca1 Si6 110.46(16) . . ? 
Si5 Ca1 Si6 131.74(17) . . ? 
Al1B Ca1 Si6 98.87(14) . . ? 
OA2F Ca2 OS1F 157.8(9) 2_846 . ? 
OA2F Ca2 O3B 99.6(8) 2_846 2_846 ? 
OS1F Ca2 O3B 87.7(6) . 2_846 ? 
OA2F Ca2 W5 30.0(10) 2_846 2_846 ? 
OS1F Ca2 W5 128.5(11) . 2_846 ? 
O3B Ca2 W5 98.4(10) 2_846 2_846 ? 
OA2F Ca2 O2 83.4(7) 2_846 2_845 ? 
OS1F Ca2 O2 84.3(6) . 2_845 ? 
O3B Ca2 O2 164.4(4) 2_846 2_845 ? 
W5 Ca2 O2 76.5(9) 2_846 2_845 ? 
OA2F Ca2 O4 100.4(8) 2_846 2_745 ? 
OS1F Ca2 O4 89.9(7) . 2_745 ? 
O3B Ca2 O4 131.3(4) 2_846 2_745 ? 
W5 Ca2 O4 120.1(10) 2_846 2_745 ? 
O2 Ca2 O4 62.2(3) 2_845 2_745 ? 
OA2F Ca2 W2 82.6(11) 2_846 . ? 
OS1F Ca2 W2 77.7(10) . . ? 
O3B Ca2 W2 82.3(8) 2_846 . ? 
W5 Ca2 W2 53.1(13) 2_846 . ? 
O2 Ca2 W2 82.9(8) 2_845 . ? 
O4 Ca2 W2 144.1(8) 2_745 . ? 
OA2F Ca2 O12B 52.7(7) 2_846 2_846 ? 
OS1F Ca2 O12B 140.5(6) . 2_846 ? 
O3B Ca2 O12B 53.1(4) 2_846 2_846 ? 
W5 Ca2 O12B 69.9(9) 2_846 2_846 ? 
O2 Ca2 O12B 134.9(4) 2_845 2_846 ? 
O4 Ca2 O12B 111.1(4) 2_745 2_846 ? 
W2 Ca2 O12B 99.2(9) . 2_846 ? 
OA2F Ca2 Al1 86.9(7) 2_846 2_745 ? 
OS1F Ca2 Al1 92.5(6) . 2_745 ? 
O3B Ca2 Al1 162.2(4) 2_846 2_745 ? 
W5 Ca2 Al1 95.4(9) 2_846 2_745 ? 
O2 Ca2 Al1 32.2(2) 2_845 2_745 ? 
O4 Ca2 Al1 30.9(3) 2_745 2_745 ? 
W2 Ca2 Al1 115.2(8) . 2_745 ? 
O12B Ca2 Al1 122.9(4) 2_846 2_745 ? 
OA2F Ca2 Si3B 79.1(7) 2_846 2_846 ? 
OS1F Ca2 Si3B 112.5(6) . 2_846 ? 
O3B Ca2 Si3B 26.1(3) 2_846 2_846 ? 
W5 Ca2 Si3B 88.7(9) 2_846 2_846 ? 
O2 Ca2 Si3B 162.5(3) 2_845 2_846 ? 
O4 Ca2 Si3B 120.2(3) 2_745 2_846 ? 
W2 Ca2 Si3B 95.6(8) . 2_846 ? 
O12B Ca2 Si3B 28.0(3) 2_846 2_846 ? 
Al1 Ca2 Si3B 144.2(2) 2_745 2_846 ? 
OA2F Ca2 Al2F 26.0(7) 2_846 2_846 ? 
OS1F Ca2 Al2F 166.3(6) . 2_846 ? 
O3B Ca2 Al2F 79.3(3) 2_846 2_846 ? 
W5 Ca2 Al2F 50.3(9) 2_846 2_846 ? 
O2 Ca2 Al2F 107.2(3) 2_845 2_846 ? 
O4 Ca2 Al2F 102.0(4) 2_745 2_846 ? 
W2 Ca2 Al2F 95.9(9) . 2_846 ? 
O12B Ca2 Al2F 27.8(3) 2_846 2_846 ? 
Al1 Ca2 Al2F 101.3(2) 2_745 2_846 ? 
Si3B Ca2 Al2F 55.5(2) 2_846 2_846 ? 
OA2F Ca2 Al1B 119.6(7) 2_846 2_846 ? 
OS1F Ca2 Al1B 63.7(6) . 2_846 ? 
O3B Ca2 Al1B 24.7(3) 2_846 2_846 ? 
W5 Ca2 Al1B 108.3(9) 2_846 2_846 ? 
O2 Ca2 Al1B 142.9(3) 2_845 2_846 ? 
O4 Ca2 Al1B 131.1(3) 2_745 2_846 ? 
W2 Ca2 Al1B 72.8(8) . 2_846 ? 
O12B Ca2 Al1B 77.7(3) 2_846 2_846 ? 
Al1 Ca2 Al1B 153.5(2) 2_745 2_846 ? 
Si3B Ca2 Al1B 50.79(12) 2_846 2_846 ? 
Al2F Ca2 Al1B 103.0(2) 2_846 2_846 ? 
O6 Si1 O1 113.9(6) . . ? 
O6 Si1 O5 110.4(6) . 2_745 ? 
O1 Si1 O5 109.3(6) . 2_745 ? 
O6 Si1 O7 110.1(6) . 2_845 ? 
O1 Si1 O7 106.0(6) . 2_845 ? 
O5 Si1 O7 106.7(6) 2_745 2_845 ? 
O10 Si2 O2 111.2(6) . . ? 
O10 Si2 O9 108.6(8) . . ? 
O2 Si2 O9 107.6(7) . . ? 
O10 Si2 O8 108.1(7) . . ? 
O2 Si2 O8 112.1(5) . . ? 
O9 Si2 O8 109.1(7) . . ? 
O12 Si3 O8 110.0(6) . . ? 
O12 Si3 O11 107.4(6) . 2_745 ? 
O8 Si3 O11 105.4(6) . 2_745 ? 
O12 Si3 O3 109.1(6) . . ? 
O8 Si3 O3 113.7(6) . . ? 
O11 Si3 O3 111.1(6) 2_745 . ? 
O13B Si4 O9B 113.3(6) . 2_846 ? 
O13B Si4 O14 112.8(6) . 2_846 ? 
O9B Si4 O14 102.2(6) 2_846 2_846 ? 
O13B Si4 O4B 114.6(6) . 2_846 ? 
O9B Si4 O4B 109.3(6) 2_846 2_846 ? 
O14 Si4 O4B 103.5(6) 2_846 2_846 ? 
O13B Si4 Ca1 137.6(5) . 2_846 ? 
O9B Si4 Ca1 109.0(4) 2_846 2_846 ? 
O14 Si4 Ca1 55.2(4) 2_846 2_846 ? 
O4B Si4 Ca1 49.1(4) 2_846 2_846 ? 
O15 Si5 O16 111.6(7) . . ? 
O15 Si5 O5B 110.1(6) . . ? 
O16 Si5 O5B 105.8(7) . . ? 
O15 Si5 O11B 106.9(7) . . ? 
O16 Si5 O11B 109.3(7) . . ? 
O5B Si5 O11B 113.3(7) . . ? 
O15 Si5 Ca1 42.9(4) . . ? 
O16 Si5 Ca1 119.6(5) . . ? 
O5B Si5 Ca1 132.8(5) . . ? 
O11B Si5 Ca1 64.4(5) . . ? 
O16B Si6 O10 108.7(7) . . ? 
O16B Si6 O7 110.8(6) . . ? 
O10 Si6 O7 112.5(6) . . ? 
O16B Si6 O14 106.1(6) . . ? 
O10 Si6 O14 103.4(7) . . ? 
O7 Si6 O14 114.9(6) . . ? 
O16B Si6 Ca1 82.0(4) . . ? 
O10 Si6 Ca1 78.3(5) . . ? 
O7 Si6 Ca1 157.9(4) . . ? 
O14 Si6 Ca1 43.0(4) . . ? 
O3 Al1 O4 109.8(6) . . ? 
O3 Al1 O1 106.0(6) . 2_755 ? 
O4 Al1 O1 113.8(6) . 2_755 ? 
O3 Al1 O2 115.7(6) . 1_455 ? 
O4 Al1 O2 96.7(6) . 1_455 ? 
O1 Al1 O2 114.8(5) 2_755 1_455 ? 
O3 Al1 Ca2 114.6(5) . 2_755 ? 
O4 Al1 Ca2 49.1(4) . 2_755 ? 
O1 Al1 Ca2 139.2(4) 2_755 2_755 ? 
O2 Al1 Ca2 49.4(4) 1_455 2_755 ? 
O6 Al2 O13 108.2(6) . . ? 
O6 Al2 O15 118.7(6) . . ? 
O13 Al2 O15 107.3(6) . . ? 
O6 Al2 O12 111.7(5) . . ? 
O13 Al2 O12 116.7(6) . . ? 
O15 Al2 O12 94.2(5) . . ? 
O6 Al2 Ca1 132.7(4) . . ? 
O13 Al2 Ca1 119.0(5) . . ? 
O15 Al2 Ca1 46.9(4) . . ? 
O12 Al2 Ca1 47.6(4) . . ? 
Si1F Si1B O1B 67.3(12) . . ? 
Si1F Si1B O6B 160.0(15) . . ? 
O1B Si1B O6B 96.9(16) . . ? 
Si1F Si1B O7B 70.0(9) . . ? 
O1B Si1B O7B 108.5(12) . . ? 
O6B Si1B O7B 128.6(15) . . ? 
Si1F Si1B O5B 64.4(8) . . ? 
O1B Si1B O5B 114.6(11) . . ? 
O6B Si1B O5B 115.6(14) . . ? 
O7B Si1B O5B 93.6(9) . . ? 
Si1B Si1F O1B 66.9(12) . . ? 
Si1B Si1F O5B 76.5(8) . . ? 
O1B Si1F O5B 122.3(11) . . ? 
Si1B Si1F OS1F 162.5(12) . . ? 
O1B Si1F OS1F 95.6(14) . . ? 
O5B Si1F OS1F 114.3(11) . . ? 
Si1B Si1F O7B 71.1(9) . . ? 
O1B Si1F O7B 108.9(11) . . ? 
O5B Si1F O7B 98.8(9) . . ? 
OS1F Si1F O7B 118.3(12) . . ? 
O2B Si2B O10B 117.7(7) 1_655 . ? 
O2B Si2B O8B 107.7(6) 1_655 . ? 
O10B Si2B O8B 107.6(7) . . ? 
O2B Si2B O9B 110.5(6) 1_655 . ? 
O10B Si2B O9B 100.5(6) . . ? 
O8B Si2B O9B 112.9(6) . . ? 
O12B Si3B O3B 105.1(9) . . ? 
O12B Si3B O8B 109.0(7) . . ? 
O3B Si3B O8B 112.4(6) . . ? 
O12B Si3B O11B 115.2(9) . . ? 
O3B Si3B O11B 105.7(6) . . ? 
O8B Si3B O11B 109.5(6) . . ? 
O12B Si3B Ca2 66.5(8) . 2_856 ? 
O3B Si3B Ca2 41.0(4) . 2_856 ? 
O8B Si3B Ca2 111.9(5) . 2_856 ? 
O11B Si3B Ca2 134.9(5) . 2_856 ? 
O13 Si4B O9 110.0(7) . 2_745 ? 
O13 Si4B O4 112.0(7) . 2_745 ? 
O9 Si4B O4 112.7(7) 2_745 2_745 ? 
O13 Si4B O14B 115.1(8) . . ? 
O9 Si4B O14B 106.9(8) 2_745 . ? 
O4 Si4B O14B 99.9(8) 2_745 . ? 
O5 Si5B O15B 113.0(6) . . ? 
O5 Si5B O16B 107.2(6) . . ? 
O15B Si5B O16B 111.0(6) . . ? 
O5 Si5B O11 108.1(6) . . ? 
O15B Si5B O11 114.4(7) . . ? 
O16B Si5B O11 102.4(6) . . ? 
O16 Si6B O7B 110.1(9) . 1_455 ? 
O16 Si6B O14B 106.6(9) . . ? 
O7B Si6B O14B 112.5(9) 1_455 . ? 
O16 Si6B O10B 111.2(6) . 2_846 ? 
O7B Si6B O10B 112.7(9) 1_455 2_846 ? 
O14B Si6B O10B 103.4(8) . 2_846 ? 
O1B Al1B O4B 121.5(9) 2_856 . ? 
O1B Al1B O2B 110.0(7) 2_856 . ? 
O4B Al1B O2B 103.1(6) . . ? 
O1B Al1B O3B 103.7(9) 2_856 . ? 
O4B Al1B O3B 103.0(5) . . ? 
O2B Al1B O3B 116.0(6) . . ? 
O1B Al1B Ca1 150.5(9) 2_856 . ? 
O4B Al1B Ca1 38.9(4) . . ? 
O2B Al1B Ca1 68.3(4) . . ? 
O3B Al1B Ca1 103.1(4) . . ? 
O1B Al1B Ca2 73.1(9) 2_856 2_856 ? 
O4B Al1B Ca2 132.1(4) . 2_856 ? 
O2B Al1B Ca2 114.1(4) . 2_856 ? 
O3B Al1B Ca2 33.8(4) . 2_856 ? 
Ca1 Al1B Ca2 135.69(18) . 2_856 ? 
Al2F Al2B O12B 76.1(11) . . ? 
Al2F Al2B O15B 78.5(10) . 2_846 ? 
O12B Al2B O15B 118.2(10) . 2_846 ? 
Al2F Al2B O6B 166.3(15) . . ? 
O12B Al2B O6B 97.2(14) . . ? 
O15B Al2B O6B 115.1(12) 2_846 . ? 
Al2F Al2B O13B 61.1(9) . . ? 
O12B Al2B O13B 108.3(8) . . ? 
O15B Al2B O13B 106.6(7) 2_846 . ? 
O6B Al2B O13B 111.1(12) . . ? 
Al2B Al2F O12B 70.4(11) . . ? 
Al2B Al2F O13B 89.3(10) . . ? 
O12B Al2F O13B 118.3(9) . . ? 
Al2B Al2F O15B 69.6(10) . 2_846 ? 
O12B Al2F O15B 111.5(9) . 2_846 ? 
O13B Al2F O15B 114.4(8) . 2_846 ? 
Al2B Al2F OA2F 157.6(14) . . ? 
O12B Al2F OA2F 89.8(12) . . ? 
O13B Al2F OA2F 109.9(11) . . ? 
O15B Al2F OA2F 110.3(11) 2_846 . ? 
Al2B Al2F Ca2 126.7(9) . 2_856 ? 
O12B Al2F Ca2 60.6(8) . 2_856 ? 
O13B Al2F Ca2 131.2(7) . 2_856 ? 
O15B Al2F Ca2 109.3(6) 2_846 2_856 ? 
OA2F Al2F Ca2 31.1(8) . 2_856 ? 
Si1 O1 Al1 146.2(7) . 2_745 ? 
Si2 O2 Al1 132.7(6) . 1_655 ? 
Si2 O2 Ca2 124.9(6) . 2_855 ? 
Al1 O2 Ca2 98.4(4) 1_655 2_855 ? 
Si3 O3 Al1 142.6(9) . . ? 
Si4B O4 Al1 135.3(8) 2_755 . ? 
Si4B O4 Ca2 123.6(7) 2_755 2_755 ? 
Al1 O4 Ca2 99.9(5) . 2_755 ? 
Si5B O5 Si1 134.9(7) . 2_755 ? 
Si1 O6 Al2 138.5(7) . . ? 
Si6 O7 Si1 134.1(7) . 2_855 ? 
Si3 O8 Si2 138.3(7) . . ? 
Si4B O9 Si2 144.0(9) 2_755 . ? 
Si6 O10 Si2 159.6(10) . . ? 
Si3 O11 Si5B 138.2(7) 2_755 . ? 
Si3 O12 Al2 126.2(7) . . ? 
Si3 O12 Ca1 132.7(7) . . ? 
Al2 O12 Ca1 100.2(5) . . ? 
Si4B O13 Al2 155.0(9) . . ? 
Si6 O14 Si4 131.2(7) . 2_856 ? 
Si6 O14 Ca1 112.7(6) . . ? 
Si4 O14 Ca1 94.8(5) 2_856 . ? 
Si5 O15 Al2 139.2(8) . . ? 
Si5 O15 Ca1 110.3(6) . . ? 
Al2 O15 Ca1 101.8(5) . . ? 
Si6B O16 Si5 159.8(9) . . ? 
Si1B O1B Si1F 45.8(7) . . ? 
Si1B O1B Al1B 149.1(17) . 2_846 ? 
Si1F O1B Al1B 159.7(18) . 2_846 ? 
Si2B O2B Al1B 142.0(8) 1_455 . ? 
Si3B O3B Al1B 125.4(7) . . ? 
Si3B O3B Ca2 112.8(6) . 2_856 ? 
Al1B O3B Ca2 121.5(6) . 2_856 ? 
Si4 O4B Al1B 142.5(7) 2_856 . ? 
Si4 O4B Ca1 101.4(5) 2_856 . ? 
Al1B O4B Ca1 115.5(5) . . ? 
Si1F O5B Si5 131.4(8) . . ? 
Si1F O5B Si1B 39.1(5) . . ? 
Si5 O5B Si1B 130.1(8) . . ? 
Si1B O6B Al2B 158(2) . . ? 
Si6B O7B Si1F 131.0(13) 1_655 . ? 
Si6B O7B Si1B 136.9(13) 1_655 . ? 
Si1F O7B Si1B 38.9(6) . . ? 
Si3B O8B Si2B 145.3(7) . . ? 
Si4 O9B Si2B 130.3(7) 2_856 . ? 
Si6B O10B Si2B 153.1(8) 2_856 . ? 
Si3B O11B Si5 134.4(8) . . ? 
Si3B O11B Ca1 128.3(7) . . ? 
Si5 O11B Ca1 86.7(5) . . ? 
Si3B O12B Al2B 151.9(16) . . ? 
Si3B O12B Al2F 169.4(11) . . ? 
Al2B O12B Al2F 33.5(5) . . ? 
Si3B O12B Ca2 85.5(8) . 2_856 ? 
Al2B O12B Ca2 122.4(10) . 2_856 ? 
Al2F O12B Ca2 91.7(10) . 2_856 ? 
Si4 O13B Al2F 152.2(8) . . ? 
Si4 O13B Al2B 134.1(8) . . ? 
Al2F O13B Al2B 29.6(5) . . ? 
Si6B O14B Si4B 128.4(11) . . ? 
Si5B O15B Al2B 148.8(9) . 2_856 ? 
Si5B O15B Al2F 129.0(8) . 2_856 ? 
Al2B O15B Al2F 31.9(5) 2_856 2_856 ? 
Si6 O16B Si5B 139.5(8) . . ? 
W5 OA2F Al2F 125(3) . . ? 
W5 OA2F Ca2 86(2) . 2_856 ? 
Al2F OA2F Ca2 122.9(13) . 2_856 ? 
Si1F OS1F Ca2 141.8(13) . . ? 
OA2F W5 Ca2 64(2) . 2_856 ? 
 
_diffrn_measured_fraction_theta_max    0.997 
_diffrn_reflns_theta_full              23.45 
_diffrn_measured_fraction_theta_full   0.997 
_refine_diff_density_max    1.147 
_refine_diff_density_min   -0.927 
_refine_diff_density_rms    0.192 